Basic Info.
Alkali Content
Alkali Free
Area Weight
18oz(600GSM)
Roll Width
1250mm
Moisture Content %
≤0.1
Loss of Ignition
0.4-0.8%
Transport Package
in Carton Box
Specification
18oz (600gsm)
Trademark
JLON
Origin
China
HS Code
70194000
Production Capacity
20000ton
Product Description
Related products:
Introduction:
Fiberglass Woven Roving is bidirectional fabric made by interweaving direct roving. Can be compatible with unsaturated polyester, vinyl ester, epoxy and phenolic resins. With high-performance reinforcement, widely used in hand lay up to manufacture boats, vessels, plane and automotive parts, furniture and sports facilities. The area weight is from 200g/m2 to 1200g/m2. The width is from 50mm-3000mm.
Specifications:
| 7628 Fiberglass Cloth | 7628 fiberglass fabric is an ultra thin and tight plain weave fabric made by E-glass fiberglass yarn (G75 1/0) . It's with a variety of applications after different surface treatment. |
3732 Fiberglass cloth | 3732 textiles made of fiberglass yarns are widely used in fields of industrial insulation, heat insulation, corrosion resistance, fire protection, coating and composite deep-processing. |
7533 Fiberglass Cloth | 7533 surfboard fiberglass cloth is plain weave fabric with sizing ensuring complete transparency when wetted out with resin. Most common is 4oz(124gsm) and 6oz(200gsm) with standard or warp enhanced. |
Glass Bulked Filter Cloth | Bulk glass fiber has been widely used in the field of filtration because of its high temperature resistance and corrosion resistance. It can be used for high temperature air filtration in cement kilns, garbage incineration, thermal power generation, iron and steel metallurgy and other industries. |
Coated Glass Mat | Coated Glass Facers RMC are designed to be used as a dimensionally stable, fire resistant substrate for many different industries. Various coatings (acrylic coating, paper pulp coating, cement coating etc.) are available that enhance adhesion to other products and weather ability. |
High Silica Glass Cloth | Silica fiberglass is a high temperature inorganic fibers that content more than 96% of SiO2, it's resistant to high temperature. For its properties of chemical stability, high temperature resistance and ablation resistance, it is widely used in aviation and aerospace, metallurgy, chemical, building material and fire fighting industry, etc... |
Introduction:
Fiberglass Woven Roving is bidirectional fabric made by interweaving direct roving. Can be compatible with unsaturated polyester, vinyl ester, epoxy and phenolic resins. With high-performance reinforcement, widely used in hand lay up to manufacture boats, vessels, plane and automotive parts, furniture and sports facilities. The area weight is from 200g/m2 to 1200g/m2. The width is from 50mm-3000mm.
Specifications:
| Product No. | Glass | Weight(g/m²) | Breaking Strength ≥N/25MM | Weave | Moisture Content % | L.O.I Content % | |
| Warp | Weft | ||||||
| WR200 | E | 200+/-10 | 820 | 700 | Plain | ≤0.1 | 0.4-0.8 |
| WR270 | E/ECR | 270+/-14 | 1200 | 1000 | Plain | ≤0.1 | 0.4-0.8 |
| WR300 | E | 300+/-15 | 1200 | 1200 | Plain | ≤0.1 | 0.4-0.8 |
| WR360 | E/ECR | 400+/-20 | 1200 | 1150 | Plain | ≤0.1 | 0.4-0.8 |
| WR400 | E | 400+/-20 | 1480 | 1380 | Plain | ≤0.1 | 0.4-0.8 |
| WR500T | E | 500+/-25 | 1800 | 1700 | Twill | ≤0.1 | 0.4-0.8 |
| WR500 | E | 500+/-25 | 1800 | 1600 | Plain | ≤0.1 | 0.4-0.8 |
| WUDT500 | E | 500+/-25 | 100 | 2900 | Plain | ≤0.1 | 0.4-0.8 |
| WUDL500 | E | 500+/-25 | 2600 | 350 | Plain | ≤0.1 | 0.4-0.8 |
| WUDL530 | E | 530+/-27 | 3200 | 800 | Plain | ≤0.1 | 0.4-0.8 |
| WR580 | E/ECR | 580+/-29 | 1900 | 1600 | Plain | ≤0.1 | 0.4-0.8 |
| WR600 | E | 600+/-30 | 1900 | 1800 | Plain | ≤0.1 | 0.4-.8 |
| WR600B | E | 600+/-30 | 1900 | 1850 | Plain | ≤0.1 | 0.4-0.8 |
| WUDL600 | E | 600+/-30 | 3100 | 350 | Plain | ≤0.1 | 0.4-0.8 |
| WR800 | E | 800+/-40 | 2600 | 2300 | Plain | ≤0.1 | 0.4-0.8 |
| WR800A | E | 864+/-43 | 2900 | 2700 | Plain | ≤0.1 | 0.4-0.8 |
| WR1000 | E | 1000+/-50 | 2900 | 2900 | Plain | ≤0.1 | 0.4-0.8 |